High Temperature Resistant FFKM Rubber O-ring
FFKM o-rings and Perfluoroelastomer materials provide the highest temperature (up to 330 oC) and most universal chemical resistance of any rubber o-ring and gasket material. FFKM o-rings are utilized in the most demanding applications with dozens of compounds engineered for targeted application performance like low or high temperature, chemical compatibility and industry compliance. Our high performance High Temperature Resistant FFKM Rubber O-ring can satisfy your need in high temperature application and save your cost much Model:KXT480E
Send Inquiry
Product Description
A series of Kalflon® FFKM O-Rings is developed by us Kaxite in order to help our customer can easily transfer from previous suppliers. Customers who used Kalrez® products before can also find their counterparts in our product list. We have chemical resistance compound FFKM O-rings series and temperature resistance compound FFKM O-rings series, and high purity FFKM series. Customized compound design is welcome by request. All data sheet can be found from our list below. We offer standard O-ring in AS-568, JIS B2401, JIS P, JIS V, JIS G, JIS S and international metric.
FFKM o-rings and Perfluoroelastomer materials provide the highest temperature (up to 330 oC) and most universal chemical resistance of any rubber o-ring and gasket material. FFKM o-rings are utilized in the most demanding applications with dozens of compounds engineered for targeted application performance like low or high temperature, chemical compatibility and industry compliance. Our high performance High Temperature Resistant FFKM Rubber O-ring can satisfy your need in high temperature application and save your cost much
Kalflon™ High Temperature Resistant FFKM Rubber Part
Equivalent product : Kalrez® 4079
|
Typical Physical Properties |
KT480E |
KT480F |
KT600E |
KT300F |
|
Hardness, Shore A |
74 |
74 |
91 |
61 |
|
Color |
Black |
Cream White |
Black |
Black |
|
100% Modulus, Mpa |
6 |
4.5 |
13.5 |
3.3 |
|
Tensile Strength at Break, Mpa |
14 |
7.5 |
16.5 |
11 |
|
Elongation at Break, % |
260 |
262 |
115 |
189 |
|
Compression Sets,(%, 70 hr @ 200 °C) |
23 |
24 |
28 |
11 |
|
Maximum Continuous Service Temp, °C |
330 |
330 |
330 |
330 |
ASTM D2240 (pellet test specimen)
ASTM D412 (dumbbell test specimen)
ASTM D395B (AS568 K214 O-ring test specimen)
ASTM D412 (dumbbell test specimens)
ASTM D395B (AS214 O-ring test specimens)
Kalflon™ Chemical Resistant FFKM Rubber Part
Equivalent product : Kalrez® 6375, Chemraz® 505
|
Typical Physical Properties |
KA480E |
KA480F |
KA482E |
KA500E |
KA600E |
KA300F |
|
Hardness, Shore A |
75 |
74 |
76 |
81 |
90 |
62 |
|
Color |
Black |
White |
Black |
Black |
Black |
White |
|
100% Modulus, Mpa |
17.5 |
4.5 |
11.6 |
11 |
17 |
4.5 |
|
Tensile Strength at Break, Mpa |
17.5 |
10 |
15.8 |
18.5 |
21 |
14.1 |
|
Elongation at Break, % |
177 |
190 |
129 |
150 |
125 |
188 |
|
Compression Sets,(%, 70 hr @ 200 °C) |
22 |
25 |
20 |
24 |
30 |
30 |
|
Maximum Continuous Service Temp, °C |
230 |
250 |
275 |
250 |
250 |
250 |
ASTM D2240 (pellet test specimen)
ASTM D412 (dumbbell test specimen)
ASTM D395B (AS568 K214 O-ring test specimen)
ASTM D412 (dumbbell test specimens)
ASTM D395B (AS214 O-ring test specimens)
Kalflon™ High-pure, low outgassing FFKM Rubber Part
Equivalent product : Kalrez® 8100, 9100, 9300
|
Typical Physical Properties |
KP300L |
KP480G |
KP500F |
KA500TF |
|
Hardness, Shore A |
65 |
74 |
76 |
81 |
|
Color |
Transparent dark |
Transparent dark |
Cream White |
White |
|
100% Modulus, Mpa |
3.3 |
6.2 |
4.7 |
8 |
|
Tensile Strength at Break, Mpa |
13 |
17 |
11.5 |
12.5 |
|
Elongation at Break, % |
215 |
251 |
303 |
178 |
|
Compression Sets,(%, 70 hr @ 200 °C) |
12.5 |
17.5 |
25 |
35 |
|
Maximum Continuous Service Temp, °C |
315 |
315 |
315 |
250 |
ASTM D2240 (pellet test specimen)
ASTM D412 (dumbbell test specimen)
ASTM D395B (AS568 K214 O-ring test specimen)
ASTM D412 (dumbbell test specimens)
ASTM D395B (AS214 O-ring test specimens)
Kalflon™ FDA Standard FFKM Rubber Part
|
Typical Physical Properties |
KF810F |
KP810E |
|
Hardness, Shore A |
65 |
74 |
|
Color |
White |
Black |
|
100% Modulus, Mpa |
5.8 |
16 |
|
Tensile Strength at Break, Mpa |
12.2 |
17.5 |
|
Elongation at Break, % |
215 |
180 |
|
Compression Sets,(%, 70 hr @ 200 °C) |
28 |
17 |
|
Maximum Continuous Service Temp, °C |
250 |
250 |
ASTM D2240 (pellet test specimen)
ASTM D412 (dumbbell test specimen)
ASTM D395B (AS568 K214 O-ring test specimen)
ASTM D412 (dumbbell test specimens)
ASTM D395B (AS214 O-ring test specimens)
Kalflon™ Low compression set, Thermal resistant FFKM Rubber Part
Equivalent product : Kalrez® 7075
|
Typical Physical Properties |
KLS410 |
KLS450 |
|
Hardness, Shore A |
74 |
74 |
|
Color |
Black |
Black |
|
100% Modulus, Mpa |
10.5 |
8.8 |
|
Tensile Strength at Break, Mpa |
15 |
12.5 |
|
Elongation at Break, % |
182 |
183 |
|
Compression Sets,(%, 70 hr @ 200 °C) |
15 |
12.5 |
|
Maximum Continuous Service Temp, °C |
250 |
330 |
ASTM D412 (dumbbell test specimen)
ASTM D395B (AS568 K214 O-ring test specimen)
ASTM D412 (dumbbell test specimens)
ASTM D395B (AS214 O-ring test specimens)